アルカリ金属塩化物添加のもとでNb_2O_5と非晶質ホウ素によるNbB_2の合成および磁化率
https://kokushikan.repo.nii.ac.jp/records/13422
https://kokushikan.repo.nii.ac.jp/records/1342234f8b6cf-e055-4808-82ee-580a6923b272
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
本文 (1.5 MB)
|
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2018-11-01 | |||||
| タイトル | ||||||
| タイトル | アルカリ金属塩化物添加のもとでNb_2O_5と非晶質ホウ素によるNbB_2の合成および磁化率 | |||||
| 言語 | ja | |||||
| タイトル | ||||||
| タイトル | Synthesis and magnetic susceptibility of NbB_2 powders by Nb_2O_5 and B with addition of alkali metal chlorides | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | departmental bulletin paper | |||||
| 関連タイトル | ||||||
| 値 | 理工学部発足10周年記念号 | |||||
| 見出し | ||||||
| 大見出し | 論文 | |||||
| 言語 | ja | |||||
| 見出し | ||||||
| 大見出し | Original Paper | |||||
| 言語 | en | |||||
| 著者 |
神津, 薫
× 神津, 薫× 山﨑, 貴× 藤ヶ谷, 浩太朗× 岡田, 繁× 宍戸, 統悦× 湯蓋, 邦夫× 吉川, 彰× 森, 孝雄 |
|||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 201101073097061738 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 200901027923457791 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 200901006845219717 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 201201025896592480 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 200901062518303655 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 200901035028474357 | |||||
| 著者ID | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | J-GLOBAL : 200901048797781160 | |||||
| 著作関係者詳細 | ||||||
| 値 | 宍戸 統悦 : 東北大学 金属材料研究所 研究支援推進員 湯蓋 邦夫: 東北大学 金属材料研究所 准教授 吉川 彰 : 東北大学 金属材料研究所 教授 森 孝雄 : 独立行政法人 物質・材料研究機構 主管研究員 |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | NbB_2（hexagonal）powders were prepared by the solid-state reaction between niobium（V^｛5+｝） oxide Nb_2O_5, and amorphous boron powders with 5 mass% AECl（AE=Li, Na, K）at reaction temperatures of 873 to 1473 K for 2 h in an argon atmosphere. When the mole ratio B/Nb_2O_5 in the starting materials was 9.0, the single phase of NbB_2 was obtained at reaction temperature of 1023 K, 600 K lower than without the additives. When the AECl was not added, the single phase of NbB_2 formed at up to 1573 K exhibited particles with a grain size of approximately 10μm in diameter. When AECl was added, the product formed at soaking temperature of 1023 K exhibited particles with a grain size of approximately 0.1μm in diameter. The lattice parameters of NbB_2 changed a=0.3111～0.3084 nm and c=0.3264～0.3308 nm. This study processes are available for the production of NbB_2 such as the thermal reduction of the Nb_2O_5 with boron for addition AECl. Magnetic susceptibility of powder samples of NbB_2 was measured by using a SQUID magnetometer in the temperature range of 300 K to 1.8 K. | |||||
| 書誌情報 |
国士舘大学理工学部紀要 en : TRANSACTIONS OF THE KOKUSHIKAN UNIVERSITY SCHOOL OF SCIENCE AND ENGINEERING 巻 11, p. 35-39, 発行日 2017-11-30 |
|||||
| 出版者 | ||||||
| 出版者 | 国士舘大学理工学部 | |||||
| ISSN | ||||||
| 収録物識別子タイプ | PISSN | |||||
| 収録物識別子 | 1882-4013 | |||||
| NCID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AA12316266 | |||||
| 論文ID(NAID) | ||||||
| 関連タイプ | isIdenticalTo | |||||
| 識別子タイプ | NAID | |||||
| 関連識別子 | 40021625194 | |||||
| NDC | ||||||
| 主題Scheme | NDC | |||||
| 主題 | 459.92 | |||||
| NDC | ||||||
| 主題Scheme | NDC | |||||
| 主題 | 436.52 | |||||
| フォーマット | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | application/pdf | |||||
| 著者版フラグ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
| キーワード | ||||||
| 主題 | NbB_2, Borothermic method, Nb_2O_5, Alkali metal chloride, Magnetic susceptibility | |||||